P(VDF-HFP)/PMMA flexible composite films with enhanced energy storage density and efficiency

Luo, B and Wang, X and Wang, H and Cai, Z and Li, L (2017) P(VDF-HFP)/PMMA flexible composite films with enhanced energy storage density and efficiency. Composites Science and Technology, 151. pp. 94-103. ISSN 0266-3538

Full text not available from this repository.

Abstract

P(VDF-HFP)/PMMA composite films were fabricated using a blending and hot-molding method and investigated using both experimental and theoretical methods. The extended Flory–Huggins model were adopted to study the Gibbs energy, miscibility, and phase composition of binary mixture, and results showed favorable interactions and compatibility between P(VDF-HFP) and PMMA. The dielectric constant and loss of blend films were reduced compared to pristine films. The ferroelectric hysteresis loops of blend films are much slimmer than that of pristine P(VDF-HFP) films. The discharged energy density of 11.2 J/cm with the efficiency of 85.8% was obtained in the P(VDF-HFP)/PMMA blend films with 42.6 vol% PMMA at the electric field of 475 MV/m. The discharged energy density of blend film is 2.6 times of that of pristine film, while the energy storage efficiency is 2.07 times higher than that of pristine film. The origin of enhancement in the dielectric energy storage properties were analyzed using Fourier transform infrared spectra and atomistic simulation. FT-IR results showed γ–phase of P(VDF-HFP) was induced in blend films with a relative amount of 93.6%, comparing with the pristine P(VDF-HFP) films. The van der Waals forces and hydrogen bonding at the interface and the chain entanglement were responsible for the miscibility and stabilization of γ–phase, strengthening the energy storage properties. 3

Item Type: Article
Subjects: UNSPECIFIED
Divisions: UNSPECIFIED
Depositing User: Cron Job
Date Deposited: 26 Feb 2021 23:44
Last Modified: 10 Apr 2021 22:51
DOI: 10.1016/j.compscitech.2017.08.013